Belzona 1111
Belzona 1111
Belzona 1111 is a cold-curing 100% solids epoxy composite reinforced with silicon steel alloy.
This material can be used ofr various applications including bonding, shimming, forming, rebuilding, wrapping, patching, sealing and filling.
It will not shrink while curing in service, allowing for exact dimensions and geometry to be achieved. Belzona 1111 ensures lasting in-service performance, accounting for temperature and pressure fluctuations, loading and stresses, impact and abrasion.
Five-year shelf life makes Belzona 1111 an invaluable stock item for many maintenance proffessionals.
Usage areas: Shafts, engine blocks, Casings, pipes, keyways, tanks, flange surfaces, propeller, rudder, bow thruster.
More Info
This material can be used ofr various applications including bonding, shimming, forming, rebuilding, wrapping, patching, sealing and filling.
It will not shrink while curing in service, allowing for exact dimensions and geometry to be achieved. Belzona 1111 ensures lasting in-service performance, accounting for temperature and pressure fluctuations, loading and stresses, impact and abrasion.
Five-year shelf life makes Belzona 1111 an invaluable stock item for many maintenance proffessionals.
Usage areas: Shafts, engine blocks, Casings, pipes, keyways, tanks, flange surfaces, propeller, rudder, bow thruster.
| TECHNICAL DATA | ||
|---|---|---|
| Mixing ratio (Base : Solidifier) | 3:1 by volume | 5:1 by weight |
| Working life | 15 minutes at 25°C (77°F) | |
| Shelf life | 5 years | |
| Dry heat resistance | 200°C (392°F) | |
| Adhesion (tensile shear) | Mild steel - 2,790 psi (19.2 Mpa) | Stainless steel - 2,960 psi (20.4 Mpa) |
| Compressive strength | 9620 psi (66.3 Mpa) at 20°C (68°F) | |
| Volume capacity | 24.3in3 (398cm3)/kg | |
| Heat distortion temperature | 53°C (127°F) at 20°C (68°F) | 91°C (195°F) at 100°C (212°F) |
| Abrasion resistance | H10 Wheels (Wet) 852 mm3 | CS17 - 24 mm3 dry |
| CURE TIMES | ||||
|---|---|---|---|---|
| Temperature | 10°C (50°F) | 15°C (59°F) | 20°C (68°F) | 25°C (77°F) |
| No loading or immersion | 3 hours | 2 1/4 hours | 1 3/4 hours | 1 hour |
| Machining and/or light loading | 4 hours | 3 hours | 2 hours | 1 1/2 hours |
| Full mechanical or thermal loading | 2 days | 1 1/2 days | 1 day | 20 hours |
| Immersion in chemicals | 4 days | 3 days | 2 days | 1 1/2 days |
| Approvals: | |
|---|---|
ABS Approval |
 |
NSF/ANSI 61 - 2018: Drinking Water System Components - Health Effects |
 |
Bureau Veritas Type Approval |
 |
WRAS Approved Material |
 |
DNV Approval |
 |
China Classification Society |
 |
Korean Registry |
 |
| LLoyd's Register |  |