Belzona 1121
Belzona 1121
Belzona 1121 is a cold-curing 100% solids epoxy composite reinforced with silicon steel alloy. It is ideal for applications in hot climates or large areas, where extended working life is required.
These materials can be used for various applications including bonding, shimming, forming, rebuilding, wrapping, patching, sealing and filling.
They will not shrink while curing in service, allowing for exact dimensions and geometry to be achieved. Belzona 1121 ensures lasting in-service performance, accounting for temperature and pressure fluctuations, loading and stresses, impact and abrasion.
Five-year shelf life makes Belzona 1121 an invaluable stock item for many maintenance proffessionals.
Usage areas: Shafts, engine blocks, Casings, pipes, keyways, tanks, flange surfaces, propeller, rudder, bow thruster.
These materials can be used for various applications including bonding, shimming, forming, rebuilding, wrapping, patching, sealing and filling.
They will not shrink while curing in service, allowing for exact dimensions and geometry to be achieved. Belzona 1121 ensures lasting in-service performance, accounting for temperature and pressure fluctuations, loading and stresses, impact and abrasion.
Five-year shelf life makes Belzona 1121 an invaluable stock item for many maintenance proffessionals.
Usage areas: Shafts, engine blocks, Casings, pipes, keyways, tanks, flange surfaces, propeller, rudder, bow thruster.
| TECHNICAL DATA | |||
|---|---|---|---|
| Mixing ratio (Base : Solidifier) | 1:1 by volume | 1,2:1 by weight | |
| Working life | 35 minutes at 25°C (77°F) | ||
| Shelf life | 5 years | ||
| Dry heat resistance | 200°C (392°F) | ||
| Adhesion (tensile shear) | Mild steel 22.8 MPa (3,300 psi) |
Aluminium 13.1 MPa (1,900 psi) |
Copper 13.8 MPa (2,000 psi) |
| Compressive strength | 86.2 Mpa (12,500 psi) at 20°C (68°F) cure | ||
| Volume capacity | 385 cm3 (23.5in3)/1 kg | ||
| Heat distortion temperature | 50°C (122°F) at 20°C (68°F) cure | 71°C (160°F) at 100°C (212°F) cure | |
| Abrasion resistance | H10 - 1,660 mm3 wet | CS17 - 55 mm3 dry | |
| CURES TIMES | ||||
|---|---|---|---|---|
| Temperature | 10°C (50°F) | 15°C (59°F) | 20°C (68°F) | 25°C (77°F) |
| No loading or immersion | 15 hours | 9 hours | 4 3/4 hours | 2 1/2 hours |
| Machining and/or light loading | 2 days | 27 hours | 16 hours | 9 hours |
| Full mechanical or thermal loading | 5 days | 3 days | 1 1/2 days | 24 hours |
| Immersion in chemicals | 12 days | 7 days | 4 days | 2 1/2 days |