Belzona 1161 is a two-component, surface-tolerant, paste grade system for repairing and rebuilding machienrt and equipment.
This fully machinable, surface-tolerant product displaces fluid from the substrate and therefore can be applied to wet and oily surfaces as well as for underwater applications.
This material does not shrink, expand or distort during cure and can be applied in thick or thin sections in one Operation. It is easy to mix and apply without the need ofr specialis tools and can be machined using conventional tools.
Usage Areas: pump casings, seawater pipework, flange surfaces, tanks, rudder, proleepeer.
This fully machinable, surface-tolerant product displaces fluid from the substrate and therefore can be applied to wet and oily surfaces as well as for underwater applications.
This material does not shrink, expand or distort during cure and can be applied in thick or thin sections in one Operation. It is easy to mix and apply without the need ofr specialis tools and can be machined using conventional tools.
Usage Areas: pump casings, seawater pipework, flange surfaces, tanks, rudder, proleepeer.
| TECHNICAL DATA | ||||
|---|---|---|---|---|
| Mixing ratio (Base : Solidifier) | 2:1 by volume | 4:1 by weight | ||
| Working life | 16 minutes at 20°C (68°F) | |||
| Shelf life | 3 years | |||
| Dry heat resistance | 208°C (401°F) | |||
| Adhesion (tensile shear) | Grit blasted Mild steel - clean and dry: 20.7 MPa (3,007 psi) |
Grit blasted Mild steel - oily: 18.9 MPa (2,735 psi) |
Abraded Mild steel - clean and dry: 14.7 MPa (2,130 psi) |
Abraded Mild steel - oily: 15.6 MPa (2,256 psi) |
| Volume capacity | 428 cm3 (26.1 in3)/1 kg | |||
| Heat distortion temperature | 47°C (117°F) at 20°C (68°F) | |||
| Abrasion resistance | H10 - 712 mm3 Wet | CS17 - 43 mm3 dry | ||
| CURES TIMES | |||||
|---|---|---|---|---|---|
| Temperature | 5°C (41°F) | 10°C (50°F) | 20°C (68°F) | 30°C (86°F) | 40°C (104°F) |
| Machining and/or light loading | 6 hours | 4 hours | 2 hours | 1 hours | 30 minutes |
| Full mechanical or thermal loading | 4 days | 2 days | 1 day | 16 hours | 12 hours |